Belakin yumbu fiber auduron na yumbu ta hanyar aiwatar da tsari ko kuma tsarin bushewa da aka sabunta ta bushe da inji. Yana da kyawawan fannoni na rigakafin Haske mai saurin saurin haɓakar iska mai nauyi, mara iyaka, da sauƙi don gina. Ana iya yanke shi da lanƙwasa ba da tsari. Don haka, yana da amfani kuma ingantacce kayan kiln da tanderce, bututu da sauran kayan juyi.

Kyakkyawan kwanciyar hankali

Juriya ga ƙonewa

Yawan aiki da yawa

Ajiya mai zafi

Kyakkyawan motsin murya da ƙarfin ƙarfin

Low shrinkage

Mai kyau spness don zaruruwa

Inganta da shigar

Sigogi na fasaha

Iri		Com	St	Hp	Haz shan had ha	Zir-Alu	Hz
Rarraba temple.		1100℃ (1983℉)	1260℃ (2300℉)	1260℃ (2300℉)	1360℃ (2480℉)	1400℃ (2550℉)	1430℃ (2600℉)
Aiki.		<1000 ℃ (2012℉)	1050℃ (1922℉)	1100℃ (2012℉)	1200℃ (2192℉)	1200℃ (1192℉)	1350℃ (2462℉)
Launi		farin launi	farin launi	farin launi	farin launi	farin launi	farin launi
Density (kg / m3)		260-320 (16-20lb / FT3)	260-320 (16-20lb / FT3)	260-320 (16-20lb / FT3)	260-320 (16-20lb / FT3)	260-320 (16-20lb / FT3)	260-320 (16-20lb / FT3)
Linear Shrinkage (%) (24 hrs)		-3 (1000℃/1832℉)	-3 (1000℃/1832℉)	-3 (1100℃/2012℉)	-3 (1250℃/2282℉)	-3 (1000℃/2012℉)	-3 (1350℃/2462℉)
A halin da ake yi na thereral (W / m.k)		0.085 (400℃/752℉) 0.132 (800℃/1472℉) 0.180 (1000℃/2012℉)	0.085 (400℃/752℉) 0.132 (800℃/1472℉) 0.180 (1000℃/2012℉)	0.085 (400℃/752℉) 0.132 (800℃/1472℉) 0.180 (1000℃/2012℉)	0.085 (400℃/752℉) 0.132 (800℃/1472℉) 0.180 (1000℃/2012℉)	0.085 (400℃/752℉) 0.132 (800℃/1472℉) 0.180 (1000℃/2012℉)	0.085 (400℃/752℉) 0.132 (800℃/1472℉) 0.180 (1000℃/2012℉)
Karfin hankali (MPA)		0.5	0.5	0.5	0.5	0.5	0.5
Sunadarai (%)	Al2o3	44	46	47-49	52-55	45-46	39-40
	Al2o3 + SiO2	96	97	99	99	-	-
	Al2o3 + Sio2 + Zro2	-	-	-	-		99
	ZRO2	-	-	-	-	.5-7	15-17
	Fe2O3	<1.2	<1.0	0.2	0.2	0.2	0.2
	Na2o + K2o	≤0.5	≤0.5	0.2	0.2	0.2	0.2
Girman (mm)		1200 * 1000m (47 "40"); 1000 * 600m (40 "36"); 900 * 600mm (24) 36 " 20-50mm (1 " / 2") kauri